Polyvinylpyridine additives for nonaqueous electrolytes activating lithium rechargeable electrochemical cells

ABSTRACT

An electrolyte comprising an organic solvent, a lithium salt, and a polymer additive comprised of repeating vinyl units joined to one or more heterocyclic amine moieties is described. The heterocyclic amine contains five to ten ring atoms, inclusive. An electrochemical cell is also disclosed. The preferred cell comprises a negative electrode which intercalates with lithium, a positive electrode comprising an electrode active material which intercalates with lithium, and the electrolyte of the present invention activating the negative and the positive electrodes.

CROSS REFERENCE TO RELATED APPLICATION

This application claims priority from U.S. provisional application Ser. No. 61/088,375, filed Aug. 13, 2008.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to an electrochemical cell having a nonaqueous electrolyte and, particularly, to a rechargeable lithium ion cell. The activating electrolyte is provided with a polymer additive comprised of repeating vinyl units joined to one or more heterocyclic amine moieties. This improves the cycle life and shelf life of the cells.

2. Description of Related Art

The use of rechargeable lithium-ion secondary cells in portable electronic equipment such as cell phones, PDAs, and laptop computers, and in small medical devices such as neurostimulators and insulin pumps has continued to increase in recent years. In the medical device industry, the requirements for these cells imposed by the Food and Drug Administration and by the device manufacturers are very stringent. In particular, it is important that these cells have a stable and predictable shelf life prior to use, so that they can receive an initial charge and be reliably placed into service. Additionally, they must be capable of being repeatedly discharged and recharged in a predictable manner during their life cycles.

Rechargeable lithium-ion secondary cells are generally comprised of a negative electrode (anode), a positive electrode (cathode) and an intermediate separator. The typical fabrication of such a cell involves winding the anode, cathode and separator to form a jellyroll, or sequentially arranging the anodes and cathodes which are provided as plates to form a cell stack. The jellyroll or cell stack is then housed in a metal (titanium or titanium alloy, stainless steel, aluminum) casing or aluminum laminated packaging film, and then filled with electrolyte. This is followed by sealing the casing by welding, or by sealing the packaging film using suitable means such as a foot sealer.

There has been considerable investigation into the use of electrolyte additives to improve cycle life and shelf life of rechargeable cells such as lithium ion cells. In particular, optimized electrolyte compositions are important to obtain lithium ion cells having improved cycle performance and shelf life. Most of the reported additives are comprised of monomers, which are intended to beneficially modify the solid electrolyte interface (SEI) layer on the anode surface during charging the cells. The formation of a surface film is unavoidable for alkali metal anodes, and in particular, lithium metal anodes and lithium intercalated carbon anodes due to their low potential and high reactivity towards organic electrolytes. Once formed, the SEI layer prevents further reaction of the electrolyte on the anode surface, thereby improving the cycle performance of the cells.

Ethylene carbonate is known to form a stable SEI layer on an anode surface at approximately 0.8V vs. Li/Li⁺. The SEI layer influences several important aspects of battery performance such as cycle life, power capability and self-discharge rate or shelf life. Preferably, the SEI layer formed on the anode surface is relatively thin and of a uniform thickness. If it is not uniform, a relatively thick SEI layer will be formed on the electrode surface due to lithium deposition on the anode. This results in poor cycle life and higher self-discharge rate due to consumption of additional electrolyte on the electrode surface.

Various electrolyte additives have been disclosed which form a passivation layer on an electrode, stabilize the passivation layer, improve thermal stability of the electrolyte and cell, and improve overcharge safety. Although the cyclic performance and shelf life of lithium ion cells has been improved significantly by using organic additives in electrolytes, there remains a considerable need for further improvements in order to satisfy the increasingly stringent performance requirements in new cell applications.

SUMMARY OF THE INVENTION

The present invention meets this need by providing a rechargeable secondary electrochemical cell having an improved electrolyte. The electrolyte is comprised of an organic solvent, an alkali metal salt, and a polymer additive comprised of repeating vinyl units joined to one or more heterocyclic amine moieties. The heterocyclic amine may contain five or six ring atoms. One preferred heterocyclic amine is pyridine, with the additive thus being poly(2-vinylpyridine). Alternatively, the additive may be a copolymer having the general formula:

wherein R¹ is a heterocyclic amine containing five or six ring atoms, and R² is an aromatic compound, or an acyrlate containing at least four carbon atoms. In the copolymer, m is preferably in the range of 20 to 100 mole percent.

The polymer additive may be present at a concentration of between about 0.05 and about 1.0 weight percent of the electrolyte, and is completely dissolved in the solvent in the described concentration range. Preferred organic solvents are carbonate solvents. The polymer additive preferably has a molecular weight of at least about 5,000.

The electrochemical cell is comprised of a negative electrode which intercalates with an alkali metal, and a positive electrode comprising an electrode active material which intercalates with the alkali metal. The preferred alkali metal is lithium. The electrodes are activated with the electrolyte comprising a lithium salt. According to the present invention, the electrolyte contains a lithium salt and poly(2-vinylpyridine) or its copolymers, or mixtures of them as an additive that improves the cycle life and shelf life of a lithium ion cell without sacrificing its capacity and rate performance.

The foregoing and additional objects, advantages, and characterizing features of the present invention will become increasingly more apparent upon a reading of the following detailed description together with the included drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will be described by reference to the following drawings, in which like numerals refer to like elements, and in which:

FIG. 1 is a graph of the cyclic performance of an exemplary cell containing an additive of vinylpyridine in comparison to a cell devoid of an electrolyte additive, both according to the prior art, and a cell with poly(2-vinylpyridine) as an electrolyte additive according to the present invention; and

FIG. 2 is a graph of the recoverable capacity of a exemplary cell, according to the present invention, and a prior art cell with no electrolyte additive, both after storage at 37° C. for seven months.

Accordingly, the present invention will be described in connection with preferred embodiments, however, it should be understood that there is no intent to limit the invention to the embodiments described. On the contrary, the intent is to cover all alternatives, modifications, and equivalents as may be included within the spirit and scope of the invention as defined by the appended claims.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

A secondary electrochemical cell constructed according to the present invention includes an anode active material selected from Groups IA, IIA, or IIIB of the Periodic Table of Elements, including the alkali metals lithium, sodium, potassium, etc. The preferred anode active material comprises lithium.

In secondary electrochemical systems, the anode or negative electrode comprises a material capable of intercalating and de-intercalating the alkali metal, and preferably lithium. A carbonaceous anode comprising any of the various forms of carbon (e.g., coke, graphite, acetylene black, carbon black, glassy carbon, carbon nanotubes, etc.) which are capable of reversibly retaining the lithium species is preferred. Alternatively, the anode active material may be a metal or metal oxide such as silicon, tin, aluminum, zinc, silver and the various oxides thereof.

Graphite is particularly preferred due to its relatively high lithium-retention capacity. Regardless of the form of the carbon, fibers of the carbonaceous material are particularly advantageous because they have excellent mechanical properties which permit them to be fabricated into rigid electrodes that are capable of withstanding degradation during repeated charge/discharge cycling. Moreover, the high surface area of carbon fibers allows for rapid charge/discharge rates. Meso-carbon microbeads (MCMB) are one preferred carbonaceous anode material.

The anode for the secondary cell is fabricated by mixing about 90 to 97 weight percent of the carbonaceous anode material with about 3 to 10 weight percent of an electrode binder material, which is preferably a fluoro-resin powder such as polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVDF), polyethylenetetrafluoroethylene (ETFE), polyamides, polyimides, and mixtures thereof. Less than 3 weight percent of the binder provides insufficient cohesiveness to the loosely agglomerated electrode active materials to prevent delamination, sloughing and cracking during electrode preparation and cell fabrication and during cell discharge. More than 10 weight percent of the binder provides a cell with diminished capacity and reduced current density due to lowered electrode active density.

This negative electrode admixture is provided on a current collector selected from copper, stainless steel, titanium, tantalum, platinum, gold, aluminum, nickel, cobalt nickel alloy, highly alloyed ferritic stainless steel containing molybdenum and chromium, and nickel-, chromium-, and molybdenum-containing alloys. The current collector is a foil or screen and contact is by casting, pressing, or rolling the admixture thereto.

The anode component further has an extended tab or lead of the same material as the anode current collector, i.e., preferably nickel contacted by a weld to a cell case of conductive metal in a case-negative electrical configuration. Alternatively, the carbonaceous anode may be formed in some other geometry, such as a bobbin shape, cylinder or pellet to allow an alternate low surface cell design.

The cathode or positive electrode of a secondary cell preferably comprises a lithiated material that is stable in air and readily handled. Examples of such air-stable lithiated cathode materials include oxides, sulfides, selenides, and tellurides of such metals as vanadium, titanium, chromium, copper, molybdenum, niobium, iron, nickel, cobalt and manganese. The more preferred oxides include LiNiO₂, LiMn₂O₄, LiCoO₂, LiCo_(0.92)Sn_(0.08)O₂ and LiCo_(1−x)Ni_(x)O₂. In another embodiment, the active material has an olivine or NASICON structure of the formula LiMPO₄ where M is one or metals from columns 4 through 13 of the Periodic Table of the Elements. Preferably, M is iron or vanadium.

Before fabrication into an electrode for incorporation into an electrochemical cell, the lithiated active material (about 90 to 97 weight percent) is preferably mixed with a conductive additive (about 1 to 10 weight percent) and a binder (about 3 to 10 weight percent). In a similar manner as with the anode, suitable conductive additives for the cathode include acetylene black, carbon black, graphite and metals such as nickel, aluminum, titanium and stainless steel in powder form. Suitable fluoro-resin binders are preferably in a powder form and include PTFE, PVDF, ETFE, polyamides, polyimides, and mixtures thereof.

To discharge such secondary cells, lithium ions comprising the cathode are intercalated into the carbonaceous anode by applying an externally generated electrical potential to recharge the cell. The applied recharging electrical potential serves to draw lithium ions from the cathode material, through the electrolyte and into the carbonaceous anode to saturate the carbon comprising the anode. The resulting Li_(x)C₆ electrode can have an x ranging from about 0.1 to about 1.0. The cell is then provided with an electrical potential and discharged in a normal manner.

An alternate secondary cell construction comprises intercalating the carbonaceous material with lithium before the anode is incorporated into the cell. In that case, the cathode body can be solid and comprise, but not be limited to, such materials as manganese dioxide, silver vanadium oxide, copper silver vanadium oxide, titanium disulfide, copper oxide, copper sulfide, iron sulfide, iron disulfide, and fluorinated carbon. However, this approach is compromised by problems associated with handling lithiated carbon outside the cell. Lithiated carbon tends to react when contacted by air.

The secondary cell of the present invention includes a separator to provide physical segregation between the anode and cathode active electrodes. The separator is of an electrically insulative material to prevent an internal electrical short circuit between the electrodes. It also is chemically unreactive with the anode and cathode active materials and both chemically unreactive with and insoluble in the electrolyte. In addition, the separator material has a degree of porosity sufficient to allow flow therethrough of the electrolyte during the electrochemical reaction of the cell. The form of the separator typically is a sheet that is placed between the anode and cathode. Such is the case when the anode is folded in a serpentine-like structure with a plurality of cathode plates disposed intermediate the anode folds and received in a cell casing or when the electrode combination is rolled or otherwise formed into a cylindrical “jellyroll” configuration.

Illustrative separator materials include fabrics woven from fluoropolymeric fibers of polyethylenetetrafluoroethylene and polyethylenechlorotrifluoroethylene used either alone or laminated with a fluoropolymeric microporous film. Other suitable separator materials include non-woven glass, polypropylene, polyethylene, glass fiber materials, ceramics, a polytetraflouroethylene membrane commercially available under the designation ZITEX (Chemplast Inc.), a polypropylene membrane commercially available under the designation CELGARD (Celanese Plastic Company, Inc.) and a membrane commercially available under the designation DEXIGLAS (C.H. Dexter, Div., Dexter Corp.).

In accordance with the present invention, an electrolyte for an electrochemical cell is provided comprising an organic solvent, an alkali metal salt, and a polymer additive. In general, the choice of an electrolyte solvent system for activating a lithium electrochemical cell, and particularly a fully charged lithium ion cell is limited due to the high potential of the cathode material (up to 4.3V vs. Li/Li⁺ for Li_(1−x)CoO₂) and the low potential of the anode material (0.01V vs. Li/Li⁺ for graphite). According to the present invention, suitable nonaqueous electrolytes are comprised of an inorganic salt dissolved in a nonaqueous solvent and more preferably a lithium salt dissolved in a mixture of organic carbonate solvents comprising dialkyl (non-cyclic) carbonates selected from dimethyl carbonate (DMC), diethyl carbonate (DEC), dipropyl carbonate (DPC), ethylmethyl carbonate (EMC), methylpropyl carbonate (MPC) and ethylpropyl carbonate (EPC), and mixtures thereof, and at least one cyclic carbonate selected from propylene carbonate (PC), ethylene carbonate (EC), butylene carbonate (BC) and vinylene carbonate (VC), and mixtures thereof. Organic carbonates are generally used in the electrolyte solvent system for such cell chemistries because they exhibit high oxidative stability toward cathode materials and good kinetic stability toward anode materials.

Preferred electrolytes according to the present invention comprise solvent mixtures of EC:DMC:EMC:DEC. Most preferred volume percent ranges for the various carbonate solvents include EC in the range of about 10% to about 50%; DMC in the range of about 5% to about 75%; EMC in the range of about 5% to about 50%; and DEC in the range of about 3% to about 45%. Electrolytes containing this quaternary carbonate mixture have a freezing point below −50° C., and lithium ion cells activated with such mixtures have very good cycling behavior at room temperature as well as very good charge/discharge cycling behavior at temperatures below −20° C.

Suitable lithium salts include LiPF₆, LiBF₄, LiAsF₆, LiSbF₆, LiClO₄, LiAlCl₄, LiGaCl₄, LiC(SO₂CF₃)₃, LiNO₃, LiN(SO₂CF₃)₂, LiSCN, LiO₃SCF₂CF₃, LiC₆F₅SO₃, LiO₂CCF₃, LiSO₃F, LiB(C₆H₅)₄, LiCF₃SO₃, and mixtures thereof. Salt concentrations typically range from about 0.8 to about 1.8 molar.

According to the present invention, an electrolyte that is suitable for activating a lithium-ion secondary cell includes a polymer additive comprised of repeating vinyl units joined to one or more heterocyclic amine moieties. The polymer additive may be present at a concentration of from about 0.05 and about 1.0 weight percent of the electrolyte, and it preferably has a molecular weight of at least about 5,000. The heterocyclic amine may contain from five to ten ring atoms, inclusive. One preferred heterocyclic amine is pyridine, with the additive therefore being poly(2-vinylpyridine). Alternatively, the heterocyclic amine of the polymer may be a substituted pyridine, quinoline, imidazole, phthalimide, pyrimidine, piperidine, pyridazine, pyrazine, triazine, triazole, thiazole, and combinations thereof.

Alternatively, the additive may be a copolymer of the general formula:

wherein R¹ is a heterocyclic amine containing five or six ring atoms, and R² is an aromatic compound, or an acyrlate containing at least four carbon atoms. In the copolymer, m is preferably in the range of 20 to 100 mole percent, with n being in the corresponding range of 0 to 80 mole percent. R¹ may be selected from the above cited heterocyclic amines. R² may be an aromatic compound or an acyrlate containing at least four carbon atoms. Exemplary compounds for R² are benzene, toluene, styrene, chlorobenzene, fluorobenzene, chlorotoluene, fluorotoluene, butylmethacrylate, and combinations thereof.

The electrolyte may also contain up to 6 weight percent of an additional additive such as vinylene carbonate, fluorinated ethylene carbonate, biphenyl, and biphenyl derivatives or cyclohexyl benzene to improve the cycle life or the safety of the cell.

The preferred form of the electrochemical cell is a case-negative design wherein the anode/cathode couple is inserted into a conductive metal casing connected to the anode current collector, as is well known to those skilled in the art. A preferred material for the casing is stainless steel, although titanium, mild steel, nickel, nickel-plated mild steel and aluminum are also suitable. The casing header comprises a metallic lid having a sufficient number of openings to accommodate the glass-to-metal seal/terminal pin feedthrough for the cathode. The anode is preferably connected to the case or the lid. An additional opening is provided for electrolyte filling. The casing header comprises elements having compatibility with the other components of the electrochemical cell and is resistant to corrosion. The cell is thereafter filled with the electrolyte solution described hereinabove and hermetically sealed, such as by close-welding a stainless steel plug over the fill hole, but not limited thereto. The cell of the present invention can also be constructed in a case-positive design.

Accordingly, the following examples describe the manner and process of an electrochemical cell according to the present invention, and they set forth the best mode contemplated by the inventors of carrying out the invention, but they are not to be construed as limiting.

EXAMPLE

By way of illustration, and in no way intended to be limiting, two exemplary cells according to the present invention were prepared. Exemplary Cell I contained an electrolyte with the polymer additive being poly(2-vinylpyridine). Exemplary Cell II contained an electrolyte with the polymer additive being poly(2-vinylpyridine-co-styrene).

The anode active material in the exemplary cells was a layered carbon material, i.e. graphite. The anode slurry was prepared by kneading the anode active material, conducting carbon and polyvinylidene fluoride binder dissolved in N-methylpyrrolidinone (NMP). The anode contained about 2 weight percent of the conducting carbon and about 5 weight percent of the binder in the solid contents of the slurry. The anode slurry was then coated on both surfaces of a copper foil using wet-coating techniques and passed through a drier to remove the NMP. After drying, the anode was pressed to obtain a coating density of from about 1.25 and about 1.70 grams per milliliter.

The cathode slurry was prepared by mixing LiCoO₂ as the cathode active material, acetylene black as the conducting carbon and polyvinylidene fluoride binder dissolved in N-methylpyrrolidinone (NMP) by using a planetary mixer. The cathode contained about 2 weight percent of the conducting carbon and about 3 weight percent of the binder in the solid contents of the slurry by weight. The cathode slurry was coated onto an aluminum current collector followed by drying and roll pressing of the electrode to obtain a coating density of from about 3.0 to about 3.8 grams per milliliter. Although polyvinylidene fluoride (PVDF) was used as a binder in the cathodes and anodes of the exemplary cells, any polymer that is stable at less than 2 volts versus lithium and is insoluble in the electrolyte could be used.

The anode, cathode and a micro-porous polyolefin separator of polyethylene were stacked to form an electrode assembly, and then placed into flexible packaging film, activated with electrolyte, and hermetically sealed.

COMPARATIVE EXAMPLE

For comparison, two cells were prepared in a similar manner as the above described present invention Cells I and II except Comparative Cell III an electrolyte additive of 2-vinylpyridine monomer and Comparative Cell IV had no polymer additive in its electrolyte.

Cells I to IV were then charged to 4.1V at a 1C-rate with a cut-off current at C/20-rate, and discharged to 2.75V at a 1C-rate. Table 1 summarizes the first cycle coulomb efficiency and voltage drop of the exemplary present invention Cells I and II and the comparative prior art Cells III and IV.

TABLE 1 Voltage Voltage Coulomb after after 1 efficiency full month Voltage of first charge storage at drop Cell Additive cycle, % to 4.1 V RT mV/day I poly(2- 88.5 4.081 4.073 0.27 vinylpyridine) II poly(2- 88.6 4.083 4.075 0.27 vinylpyridine- co-styrene) III vinylpyridine 87.0 4.066 4.034 1.07 IV no additive 88.5 4.081 4.066 0.50

Exemplary Cells I and II containing a polymer additive of the present invention had a reduced voltage drop during the one month storage period, and a similar coulomb efficiency compared to the additive free Cell IV. This indicates that the polymer additives in the exemplary cells improved their shelf life. In contrast, the 2-vinylpyridine monomer additive increases the voltage drop of Cell III and reduces its coulomb efficiency.

Without wishing to be bound to any particular theory, it is believed that these diminished discharge characteristics can be attributed to decomposition of the 2-vinylpyridine monomer additive forming a thick insulation layer on the anode surface-electrolyte-interface (SEI). This SEI layer accelerates lithium deposition at the anode, resulting in poor cycle life and a higher self discharge rate due to consumption of additional electrolyte on the anode surface.

FIG. 1 depicts the cyclic performance of the exemplary present invention Cell I and the comparative prior art Comparative Cells III and IV. It can be seen that the exemplary cell activated with an electrolyte containing the poly(2-vinylpridine) additive according to the present invention showed superior cyclic performance compared to the additive free cell and the cell activated with an electrolyte containing vinylpyridine monomer additive, which showed extremely poor cyclic performance.

FIG. 2 depicts the recoverable capacity of the Cells I to IV after storage at 37° C. for seven months. The cells were discharged and charged three times each month at C/5-rate during storage at 37° C. to obtain the recoverable capacity of the cells, and then stored again at 37° C. at a fully charged state (4.1V). The exemplary present invention Cell I with the electrolyte containing the poly(2-vinylpridine) additive had almost 90% of recoverable capacity, which is superior to the approximately 86% of recoverable capacity of the additive free cell.

It is, therefore, apparent that there has been provided, in accordance with the present invention, a rechargeable secondary electrochemical cell having an improved electrolyte. The electrolyte includes a polymer additive comprised of repeating vinyl units joined to one or more heterocyclic amine moieties. While this invention has been described in conjunction with preferred embodiments thereof, it is evident that many alternatives, modifications, and variations will be apparent to those skilled in the art. Accordingly, the present invention is intended to embrace all such alternatives, modifications and variations that fall within the broad scope of the appended claims. 

1. An electrolyte for an electrochemical cell comprising: a) an organic solvent; b) a lithium salt; and c) a polymer additive comprised of repeating units of:

wherein R¹ is a heterocyclic amine containing from five to ten ring atoms, inclusive.
 2. The electrolyte of claim 1 wherein the heterocyclic amine is selected from the group consisting of pyridine, substituted pyridine, quinoline, imidazole, phthalimide, pyrimidine, piperidine, pyridazine, pyrazine, triazine, triazole, thiazole, and combinations thereof.
 3. The electrolyte of claim 1 wherein the polymer additive is poly(2-vinylpyridine).
 4. The electrolyte of claim 1 wherein the polymer additive is comprised of repeating units of:


5. The electrolyte of claim 4 wherein R² is an aromatic compound.
 6. The electrolyte of claim 4 wherein R² is an acyrlate containing at least four carbon atoms.
 7. The electrolyte of claim 4 wherein R² is selected from the group consisting of benzene, toluene, styrene, chlorobenzene, fluorobenzene, chlorotoluene, fluorotoluene, butylmethacrylate, and combinations thereof.
 8. The electrolyte of claim 4 wherein m is in a range of 20 to 100 mole percent.
 9. The electrolyte of claim 1 wherein the polymer additive is present at a concentration of from about 0.05 to about 1.0 weight percent of the electrolyte.
 10. The electrolyte of claim 1 wherein the polymer additive is dissolved in the solvent.
 11. The electrolyte of claim 1 wherein the polymer additive has a molecular weight of at least 5,000.
 12. The electrolyte of claim 1 wherein the organic solvent comprises at least one carbonate.
 13. The electrolyte of claim 12 wherein the organic solvent is selected from the group consisting of dimethyl carbonate, diethyl carbonate, dipropyl carbonate, ethylmethyl carbonate, methylpropyl carbonate, ethylpropyl carbonate, propylene carbonate, ethylene carbonate, butylene carbonate, and mixtures thereof.
 14. The electrolyte of claim 1 wherein the lithium salt is selected from the group consisting of LiPF₆, LiBF₄, LiAsF₆, LiSbF₆, LiClO₄, LiAlCl₄, LiGaCl₄, LiC(SO₂CF₃)₃, LiNO₃, LiN(SO₂CF₃)₂, LiSCN, LiO₃SCF₂CF₃, LiC₆F₅SO₃, LiO₂CCF₃, LiSO₃F, LiB(C₆H₅)₄, LiCF₃SO₃, and mixtures thereof.
 15. The electrolyte of claim 1 further comprising an additional additive selected from the group consisting of vinylene carbonate, fluorinated ethylene carbonate, biphenyl, substituted biphenyls, cyclohexyl benzene, and combinations thereof.
 16. An electrochemical cell comprising: a) a negative electrode which intercalates with lithium; b) a positive electrode comprising an electrode active material which intercalates with lithium; and c) an electrolyte activating the negative and the positive electrodes, the electrolyte comprising an organic solvent, a lithium salt, and a polymer additive comprised of repeating units of:

wherein R¹ is a heterocyclic amine containing from five to ten ring atoms, inclusive.
 17. The electrochemical cell of claim 16 wherein the heterocyclic amine is selected from the group consisting of pyridine, substituted pyridine, quinoline, imidazole, phthalimide, pyrimidine, piperidine, pyridazine, pyrazine, triazine, triazole, thiazole, and combinations thereof.
 18. The electrochemical cell of claim 16 wherein the polymer additive is poly(2-vinylpyridine).
 19. The electrochemical cell of claim 16 wherein the polymer additive is comprised of repeating units of:


20. The electrochemical cell of claim 19 wherein R² is selected from the group consisting of benzene, toluene, chlorobenzene, fluorobenzene, chlorotoluene, fluorotoluene, acyrlates containing at least four carbon atoms, and combinations thereof.
 21. The electrochemical cell of claim 19 wherein m is in a range of 20 to 100 mole percent.
 22. The electrochemical cell of claim 16 wherein the polymer additive is present at a concentration of from about 0.05 to about 1.0 weight percent of the electrolyte.
 23. The electrochemical cell of claim 16 wherein the polymer additive has a molecular weight of at least 5,000.
 24. The electrochemical cell of claim 16 wherein the organic solvent is selected from the group consisting of dimethyl carbonate, diethyl carbonate, dipropyl carbonate, ethylmethyl carbonate, methylpropyl carbonate, ethylpropyl carbonate, propylene carbonate, ethylene carbonate, butylene carbonate, and mixtures thereof.
 25. The electrochemical cell of claim 16 wherein the lithium salt is selected from the group consisting of LiPF₆, LiBF₄, LiAsF₆, LiSbF₆, LiClO₄, LiAlCl₄, LiGaCl₄, LiC(SO₂CF₃)₃, LiNO₃, LiN(SO₂CF₃)₂, LiSCN, LiO₃SCF₂CF₃, LiC₆F₅SO₃, LiO₂CCF₃, LiSO₃F, LiB(C₆H₅)₄, LiCF₃SO₃, and mixtures thereof.
 26. A method for making an electrochemical cell, comprising the steps of: a) providing a negative electrode which intercalates with lithium; b) providing a positive electrode comprising an electrode active material which intercalates with the lithium; c) activating the negative and positive electrodes with a nonaqueous electrolyte, the electrolyte comprising an organic solvent, a lithium salt, and a polymer additive comprised of repeating units of:

wherein R¹ is a heterocyclic amine containing from five to ten ring atoms, inclusive.
 27. The method of claim 26 including selecting the heterocyclic amine from the group consisting of pyridine, substituted pyridine, quinoline, imidazole, phthalimide, pyrimidine, piperidine, pyridazine, pyrazine, triazine, triazole, thiazole, and combinations thereof.
 28. The method of claim 26 including providing the polymer additive as poly(2-vinylpyridine).
 29. The method of claim 26 including providing the polymer additive being comprised of repeating units of:


30. The method of claim 29 including selecting R² from the group consisting of benzene, toluene, chlorobenzene, fluorobenzene, chlorotoluene, fluorotoluene, acyrlates containing at least four carbon atoms, and combinations thereof.
 31. The method of claim 29 wherein m is in a range of from about 20 to about 100 mole percent.
 32. The method of claim 26 including providing the polymer additive at a concentration of from about 0.05 and about 1.0 weight percent of electrolyte.
 33. The method of claim 26 including providing the polymer additive having a molecular weight of at least 5,000.
 34. The method of claim 26 including selecting the organic solvent from the group consisting of dimethyl carbonate, diethyl carbonate, dipropyl carbonate, ethylmethyl carbonate, methylpropyl carbonate, ethylpropyl carbonate, propylene carbonate, ethylene carbonate, butylene carbonate, and mixtures thereof.
 35. The method of claim 26 including selecting the lithium salt from the group consisting of LiPF₆, LiBF₄, LiAsF₆, LiSbF₆, LiClO₄, LiAlCl₄, LiGaCl₄, LiC(SO₂CF₃)₃, LiNO₃, LiN(SO₂CF₃)₂, LiSCN, LiO₃SCF₂CF₃, LiC₆F₅SO₃, LiO₂CCF₃, LiSO₃F, LiB(C₆H₅)₄, LiCF₃SO₃, and mixtures thereof. 